DC Accelerated Aging Characteristics of $ZnO-Pr_{6}O_{11}$ Based Varistor Ceramics

$ZnO-Pr_{6}O_{11}$계 바리스터 세라믹스의 직류가속열화 특성

The stability against DC accelerated aging stress of $Dy_{2}O_{3}-doped$ $ZnO-Pr_{6}O_{11}-based$ varistor ceramics was investigated. The calculated nonlinear exponent$(\alpha)$ in varistor ceramics without $Dy_{2}O_{3}$ was only 4.9, whereas the $\alpha$ value of the varistors with $Dy_{2}O_{3}$ was abruptly increased in the range of 48.8 to 58.6. The varistor ceramics with $Dy_{2}O_{3}$ content of 1.0 mol% exhibited maximum ${\alpha}$, reaching 58.6, whereas they exhibited very poor stability. While, The varistor ceramics doped with 0.5 mol% $Dy_{2}O_{3}$ exhibited not only the high nonlinearity, which the ${\alpha}$ is 55.3 and the leakage current is $0.1{\mu}A$， but also the highest stability, which the variation rates of varistor voltage and nonlinear exponent are -0.8% and -14.3%, respectively, under DC accelerated aging stress, $0.95 V_{1mA}/150^{\circ}C/24h$.