Abstract
Ferroelectric $Bi_{4-x}Nd_xTi_3O_{12}$(BNdT) thin films with the composition(x=0.75) were prepared on pt/Ti/$SiO_2$/Si(100) substrate by metal-organic deposition. The electrical and structural characteristics of BNdT thin films were investigated to develop ferroelectric thin films for capacitor layers of FRAM. After spin coating, thin films were annealed at $650^{\circ}C$ for 1hour in oxygen atmosphere. Scanning electron micrographs showed uniform surfaces composed of rod-like grains. The $Bi_{4-x}Nd_xTi_3O_{12}$(X=0.75) thin film capacitors with a Pt top electrode showed better ferroelectric properties. At the applied voltage of 5V, the dielectric constant$(\varepsilon_r)$, dissipation factor$(tan{\delta})$, remanent polarization(2Pr) and nonvolatile swiching charge of the $Bi_{4-x}Nd_xTi_3O_{12}$(x=0.75)thin films were about 346.7, 0.095, $56{\mu}C/cm^2$ and $38{\mu}C/cm^2$ respectively. Also the capacitor did not show any significant fatigue up to $8{\times}10^{10}$ read/write switching cycles at a frequency of 1MHz.