The microwave dielectric properties of $Bi_{(1-x)}Tm_xNbO_4$

마이크로파 유전체 $Bi_{(1-x)}Tm_xNbO_4$의 유전특성

The microwave dielectric properties and the microstructures of $Tm_2O_3$-modified $BiNbO_4$ ceramics were investigated. $Bi_{(1-x)}Tm_xNbO_4$ ceramics combined with orthorhombic and triclinic phases were identified at sintering temperatures of $920{\sim}960^{\circ}C$. The apparent density decreased slightly with the increasing Tm content. Regardless of the Tm content the dielectric constant $(\varepsilon_r)$ of all compositions except x=0.1 in $Bi_{(1-x)}Tm_xNbO_4$ ceramics saturated at the range of 42~44. The $Q{\times}f_0$ values of 6,000-12,000(GHz) were obtained for all compositions when the sintering temperatures were in the range of $920{\sim}960^{\circ}C$. The temperature coefficient of the resonant frequency$(\tau_f)$ can be also adjusted with increasing the amount of the doped Tm from a positive value of $+15ppm/^{\circ}C$ to a negative value of $-20ppm/^{\circ}C$. The $Bi_{(1-x)}Tm_xNbO_4$ ceramics can be possibly applied to multilayer microwave devices with low processing temperatures.