Abstract
The degradation behaviour of ZPCCL-based varistor ceramics composed of 97.5 mol%ZnO-0.5 mol% $Pr_6O_{11}-1.0$ mol% $Cr_2O_3-0.5$ mol% $La_2O_3$ was investigated under various DC accelerated aging streses. The varistor ceramics sintered for 1 h exhibited excellent nonlinearity, in which the nonlinear exponent is 81.6 and the leakage current is $0.2{\mu}A$. It was found that this varistor ceramics possess high stability, in which the variation rates of varistor voltage, nonlinear exponent, and leakage current are -1.14%, -3.7%, and 85.0%, respectively, against DC accelerated aging stress. On the contrary, the varistor ceramics sintered for 2 h also exhibited high nonlinearity and stability, but they were bad characteristics, compared with the varistor ceramics sintered for 1 h.