Abstract
Two companies plating baths were selected for plating on phenol and epoxy resin boards as well as on flexible p polyimide boards. After plating, deposited i&IIk&.ness al1d physical properties, as well as solder wettabilities by aging with $150^{\circ}C$ heating and 100% humidity were compared. After plating and aged with two different tin baths, deposited thickness and physical properties were not so great differences, but solder wettabilities were superior used polymer catalyst than the other. Furthermore depend upon the compactness and fineness of metallic sturctures of the base copper, the amounts of the plated copper were big differel1lces. These differences seems to be inherited from the kind and amount of additives. as well as current densities, which are influences upon structures of Copper layers. Generally the tin thickness are hetween 0.5 to $1.0\mu\textrm{m}$ and thicker the solder wettabilities are the better, and also me compact structures of deposits showed gooo soidierabiiities. In this study, with our own deveiotaedl plating equipment could get more than $0.5\mu\textrm{m}$ of till thickness and piating speed was $0.1\mu\textrm{m}$ per minutes.