Leaching Behavior of LD Slag

LD slag, that is, a by-product of steel making process, has been mainly used as land construction materials. Recently, the seashore application of LD slag was tried in Japan and Korea tut the reaction between LD slag and seawater was not studied yet. We tried to clarify the leaching reaction and/or mechanism of LD slag and the reaction between seawater and LD slag. We tried to apply these results to the decarbonization of seawater for seawater magnesia process. At first, LD slag was milled and classified into 5 grades, that is, (ⅰ)45${\mu}{\textrm}{m}$ under, (ⅱ)0.25~0.5mm (ⅲ)0.5~1mm(ⅳ)1~2mm, (ⅴ)2.36~3.35mm. These slags were leached in the distilled water. In case of 45${\mu}{\textrm}{m}$ under, the pH of the leached solution was over 12. The chemical analysis of leached solution showed that the $Ca^{+}$$^2$was main component and the S $i^{+}$$^4$was very low. On the other hand, the content of S $i^{+}$$^4$in leached solution was decreased with the increase of pH of this solution. The nearly pure calcium solution was made and the ultra high purity MgO could be made with this calcium solution. The leaching behavior of LD slag was different between the fine particle and coarse particle. The calcium was leached by bulk dissolution in the coarse particle and by surface controlled reaction in fine particle. The leaching rate was slow in coarse particle and fast in fine particle. Therefore, the high pH solution, that is, over 12, was obtained in fine particle.cle.e.