An Investigation on the Shot Peening on the Low.High Temperature Fatigue Crack Propagation

쇼트피이닝 가공된 스프링강의 저.고온 피로균열진전 평가

In this study, CT specimens were prepared from spring steel(SUP9) processed shot peening which was room temperature, low temperature and high temperature experiment. And we got the following characteristics from fatigue crack growth test carried out in the environment of room, low temperature and high temperature at $25^{\circ}C$, -3$0^{\circ}C$, -5$0^{\circ}C$, -7$0^{\circ}C$, -10$0^{\circ}C$ and 5$0^{\circ}C$, 10$0^{\circ}C$ , 15$0^{\circ}C$, 18$0^{\circ}C$ and in the range of stress ratio of 0.05 by means of opening mode displacement. The threshold stress intensity factor range $\DeltaK_{th}$ in the early stage of fatigue crack growth (Region I ) and stress intensity factor range ΔK in the stable of fatigue crack growth (Region II) was decreased in proportion to descend temperature. It assumed that the fatigue resistance characteristics and fracture strength at low temperature and high temperature is considerable higher than that of room temperature in the early stage and stable of fatigue crack growth region.