초록
Zirconia powder containing 3 mol% yttria(3Y-PSZ) with and with out Fe$_2$O$_3$ addition was coated on tile cast iron substrate by plasma spraying method. The erosion experiments were performed at temperatures from $25^{\circ}C$ to $600^{\circ}C$. A gas blast type erosion tester was used to examine erosion behavior of the specimens. The results of 3Y-PSZ coatings showed that tile erosion rate had maximum value at 40$0^{\circ}C$. It coincided with tile results of phase transformation tetragonal phase to monoclinic phase caused by low temperature thermal degradation. The tensile stress relaxation and the micro-hardness improvement significantly influenced on the erosion rate at $600^{\circ}C$. In the case of Fe$_2$O$_3$ added 3Y-PSZ coatings, the erosion rate of tested at $25^{\circ}C$ showed maximum value at 5.0 mol% Fe$_2$O$_3$ added coating. This tendency is caused by the improvement of mechanical properties and the tensile residual stress. The erosion rate at 200'c and 400'L showed significantly decrease by Fe203 addition. This decrease is believed to be the stabilization of the tetragonal phase and the increase of micro-hardness.