Tribological characteristics of WC/C multilayer films with various environments

WC/C 박막 코팅의 환경변화에 따른 트라이볼로지적 특성

The friction and wear behaviors of WC/C multilayer coating were investigated by using a pin on disk type tester. The experiment was conducted by using silicon nitride (S $i_{3}$ $N_{4}$) as a pin material and WC/C multilayer coating on bearing steel (STB2) as a disk material, under various environments that are atmospheric conditions of high vacuum( 1,3$\times$10$^{-4}$ Pa), medium vacuum( 1.3$\times$10$^{-l}$Pa). ambient air( 10$^{5}$ pa)(3 types) and relative humidity(2~98%) conditions. The results showed that WC/C coating fracture was suddenly increased with increasing degree of vacuum, because of high adhesion. So, WC/C coating could not be displayed their ability as solid lubricant. WC/C coating could be displayed better abilitv as solid lubricant with increasing relative humidity. because of oxide film, size and shape of wear debris. The friction coefficient and specific wear rate became better about RH 50%.%.