Sn계 무연 솔더에 관한 연구

  • 발행 : 2001.11.01

초록

Three different kinds of substrate used in this study : bare Cu substrate, Ni-P/Cu substrate with a Ni-P layer thickness of $5\mu\textrm{m},$ and Au/Ni-P/Cu substrate with the Ni-P and Au layers of $0.15\mu\textrm{m}$ and $5\mu\textrm{m}$ thickness respectively. The wettability of various Sn-base solders was affected by the substrate metal finish used, i.e., nickel, gold and copper. On the Au/Ni-F/Cu substrate, Sn-base solders wet better than any of the other substrate metal finishes tested. The interfacial reaction between various substrate and Sn-base solder was investigated at $70^{\circ}C,$ $100^{\circ}C,$ $120^{\circ}C,$ $150^{\circ}C,$ $170^{\circ}C$ and $200^{\circ}C$ for reaction times ranging from 0 day to 60 day. Intermetallic phases was formed along a Sn-base solder/ various substrate interface during solid-state aging. The apparent activation energy for growth of Sn-Ag/Cu, Sn-Ag-Bi/Cu, and Sn-Bi/Cu couples were 65.4, 88.6, and 127.9 Kj/mol, respectively. After isothermal aging, the fracture surface shoved various characteristics depending on aging temperature and time, and the types of BGA pad.

키워드