극박 3%규소강에서 Mn이 황의 편석 거동 및 자성특성에 미치는 효과

Effects of Mn on Sulfur Segregation and Magnetic Induction in Thin-gauged 3%Si-Fe Strip

Effects of addition of manganese and final reduction on segregation behavior of sulfur and final mangetic induction during final annealing have been investigated in the 300 ppm sulfur-contained 3% silicon-iron alloy strips with or without manganese. At the same concentration of sulfur, lower final reduction is favorable for final Goss texture. This is because the probability that the initial Goss grains survive under the highly segregated sulfur atmosphere and grow selectively within the segregated sulfur-free time range becomes higher. In the case of 3% silicon-iron with manganese, much lower magnetic induction was obtained, although the weak final reduction of 30% is given to the alloy, comparative to the 40%. This is because MnS particles acted as an reducer in the primary grain size.