Heat Treatment Condition for Preparing $Nd_{1+x}Ba_{2-x}Cu_{3}O_{7-\delta}$ Superconductors

Two kinds of Nd$_{1+x}$Ba$_{2-x}$Cu$_3$O$_{7-{\delta}}$, the sintering samples and zone melting samples, were heat treated under pure Ar at 95$0^{\circ}C$. The substitution of Nd ion for Ba ion in the Nd$_{1+x}$Ba$_{2-x}$Cu$_3$O$_{7-{\delta}}$ before and after the heat treatment were investigated by XRD. In order to know the effects of the heat treatment, the T$_{c}$ and J$_{c}$ of samples with the heat treatment and those without the heat treatment by Ar were comparatively studied. The results show that the substitution of Nd for Ba decreased, T$_{c}$, and J$_{c}$ increased after the treatment under Ar at 95$0^{\circ}C$. The Nd$_{1+x}$Ba$_{2-x}$Cu$_3$O$_{7-{\delta}}$ samples were oxygenated under pure oxygen at 30$0^{\circ}C$. From the XRD pattern it was found that the sample with x< 0.4 could transfer from tetragonal phase to orthorhombic phase after the oxygenation, but the sample with x>0.4 could not make the phase transition even after a long time oxygenation.ion even after a long time oxygenation.ation.n.ation.ation.