Microwave Dielectric Properties of the (1-x)MgxSr$TiO_3$(x=0.03~0.04) ceramics

(1-x)MgxSr$TiO_3$(x=0.03~0.04) 세라믹스의 마이크로파 유전특성

The (1-x)MgTiO$_3$-xSrTiO$_3$(x=0.03~0.04) ceramics were fabricated by the conventional mixed oxide method. The sintering temperature and time were 125$0^{\circ}C$~135$0^{\circ}C$, 2hr., respectively. From the X-ray diffraction patterns, it was found that the perovskite SrTiO$_3$ and ilmenite MgTiO$_3$ structures coexisted in the (1-x)MgTiO$_3$-xSrTiO$_3$(x=0.03~0.04) ceramics. The dielectric constant($\varepsilon$$_{r}$) was increased with addition of SrTiO$_3$. The temperature coefficient of resonant frequency($\tau$$_{f}$) was gradually varied from negative value to the positive value with increasing the SrTiO$_3$. The negative temperature coefficient of resonant frequency of the magnesium titanate was adjusted to near zero at x=0.036, where the dielectric constant, quality factor, and $\tau$$_{f}$ were 20.65, 95120, and +1.3ppm/$^{\circ}C$, respectively. The temperature stability of qualify factor in (1-x)MgTiO$_3$-xSrTiO$_3$(x=0.03~0.04) ceramics increased as the amount of MgTiO$_3$./TEX>.