초록
Spinel phase LiF $e_{y}$M $n_{2-y}$ $O_4$samples are synthesized by calcining a LiOH.$H_2O$, Mn $O_2$and F $e_2$ $O_3$mixture at 80$0^{\circ}C$ for 36h in air. Preparing LiF $e_{y}$M $n_{2-y}$ $O_4$showed spinel phase with cubic phase. The ununiform distortion of the crystallite of the spinel LiF $e_{y}$M $n_{2-y}$ $O_4$was more stable than that of the pure. The discharge capacity of the cathode for the Li/LiF $e_{0.1}$M $n_{1.9}$ $O_4$cell at the first than that of the pure. The discharge capacity of the cathode for the Li/LiF $e_{0.1}$M $n_{1.9}$ $O_4$cell at the first cycle and at the 70th cycle was about 113 and 90mAh/g, respectively. This cell capacity was retained about 82% of the first cycle after 70th cycle. Impedance profile of this cell was more stable than that pure. The resistance, the capacitance and chemical diffusion coefficients of lithium ion showed approximately 80$\Omega$, 36133.87$\mu$F ; 1.4$\times$10$^{-8}$ c $m^2$ $s^{-1}$ , respectively. , respectively.ely.