Abstract
In this study, (Ba, Sr)$TiO_3$ (BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/$TiO_2$/Si substrate at 4000 [rpm] for 10 seconds. Coated specimens were dried at 150[$^{\circ}C$] for 5 minutes. Coating process was repeated 3 times and then sintered at 750[$^{\circ}C$] for 30 minutes. Structure and electrical characteristics of specimen was analyzed by Fractal Process. Thickness of BST ceramics thin films are about 2800[$\AA$]. Dielectric constant and loss of thin films was little decreased at 1[kHz]~1[MHz]. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. The property of leakage current as the relation between the current and the voltage was that change of the leakage current was stable when the applied voltage was 0~3[V].