Effect of $Al_2O_3$ Additives on Microwave Dielectric Properties of (Ba,Ca,Mg)-$Nd_2O_3-TiO_2+10wt%Bi_2O_3$ Ceramics

$Al_2O_3$ 첨가가 (Ba,Ca,Mg)-$Nd_2O_3-TiO_2+10wt%Bi_2O_3$ 세라믹의 마이크로파 유전특성에 미치는 영향

Effect of $Al_2O_3$ Additives on Microwave Dielectric Properties of $0.15(Ba_{0.85}Ca_{(0.15-y)}Mg_y)$-0.125 $Nd_2O_3-0.60TiO_2+10wt%Bi_zO_3$ (y=0.05, 0.08) Ceramics was investigated. To control of $\tau\;{f}$ on microwave dielectric properties of $0.15(Ba_{0.85}Ca_{(0.15-y)}Mg_y)$-0.125 $Nd_2O_3-0.60TiO_2+10wt%Bi_zO_3$ ceramics $Al_2O_3$ was doped in the composition range of 0 to 0.15 wt%. As a result, dielectric constant was decreased from 94 to 80 but $Q\cdot{f}_0$ value was increased from 4980 to 5210 GHz and temperature coefficient of resonant frequency can be controlled from +9 to -10$ppm^\circ{C}$ as an increase of$Al_2O_3$ doping concentration. Especially, a new microwave dielectric material having $\varepsilon\;_r=84,\;Q\cdot{f}_0=5120\;GHz\;and\;\tau_f=0\;ppm/^\circ{C}$ was obtained at $Al_2O_3$ doping concentration of 0.08 wt%.