Abstract
The ($0.8BaTiO_3-0.1SrTiO_3-0.1MgTiO_3$)+$0.006Nb_2O_5$ ceramics were fabricated by conventional ceramic process. The dielectric property of specimen was investigated that the specimen was sintering temperature at 1,300C for 3hours and then annealed at $1,100^{\circ}C$ for 3hours in a atmosphere (air) to be painted on the surface with CuO paste. The results of the temperature and frequency are varied, the dielectric constant and loss tangent are unsuitable for BL capacitor. The dielectric constants were varied to be negative temperature coefficient(2.000-3,000) in the temperature range between -10 and $140^{\circ}C$, the dissipation factors (tan $\delta$) were some high(0.1-0.3). It was not grain insulation, in cause of the some difficult to be annealed temperature with CuO paste and fired atmosphere. But, we have some different annealing temperature and fired atmosphere, it will be suitable BL(Boundary Layer)capacitor.