Effects of Sputtering pressure on preferred Orientation of Shielding NbTi Thin Film by RF Magnetron Sputtering

RF 마그네트론 스퍼터링법으로 제조된 차폐용 NbTi박막의 우선방향에 미치는 스퍼터링 압력의 영향

NbTi thin films were prepared on Si wafer and Cu substrate by rf magnetron sputtering in the range of sputtering pressure $3{\times}10^{-2}$torr to $3{\times}10^{-4}$torr at room temperature. The influence of sputtering pressure and substrate type on crystallographic orientation and morphology of NbTi thin films was investigated by using X-ray diffraction(XRD) and scanning electron microscopy(SEM), respectively. And the effect of crystallographic orientation and morphology of NbTi film on electromagnetic behaviors was estimated by measuring critical current in various applied magnetic field. The film morphology changed from porous structure consisting of tapered crystallites to densely deposited film decreasing with sputtering pressure. The change of crystallographic orientation with the sputtering pressure and rf power was calculated from the texture coefficient of(002) plane based on XRD patterns. It was found that a change of texture coefficient of(002) plane increased with decreasing sputtering pressure. From observation of critical current in various applied magnetic field, we have identified that the change of critical current abruptly decrease applying with magnetic field and NbTi film produced at high sputtering pressure does not exhibit superconductivity but at low sputtering pressure shows superconductivity.