Cure Kinetics and chemorology of silica filled DGEBA/Polyxoypropylenediamine epoxy system

무기물이 충진된 에폭시수지의 경화반응과 유변학적 거동에 관한 연구

  • Published : 1994.11.01

Abstract

The chemorheological changes and kinetics during curing reaction of an silica filled epoxy system (DGEBA with curing agent Polyxoypropylenediamine) were investigated. This study concentrates on the influence of silica on the reaction kinetics and rheological behavior of the eopxy system. The concentration of the filler was varied 0~200phr. Curing behavior of the silica filled epoxy system was measured at various heating rates with DSC. Conversion was also measured by integrating the obtained DSC curve and Kinetic parameters measured by using the nonlinear regression method. DSC experiments showed that the presence of silica was found to accelerate the progress of the curing reaction and of reduce the heat of reaction compared with that of unfilled epoxy systems . Rheological experiments were conducted on a Physica by using a disposable parallel plate fixture. Material properites were measured such as the elastic modulus(G′), the loss modulus(G"), the loss tangent(tan $\delta$), and the viscosity was at the initial stahe, and the more the silica filler was added, and the lower the gel temperature was in the epoxy system. In this study it is concluded that the curing of the silica filled epoxy system was found to be accelerated, as silica was added to the epoxy compound.

Keywords