초록
We studied chemical reactio of Eu metal on the in situ cleaved CdTe(110) surface by pphotoemission sppectroscoppy using synchrotron radiation. The chamber was maintained with base ppressure $\leq$2${\times}$10-10 mb during the expperiment. The expperiment was carried out in pphoton Factory in Jappan. Core level pphotoemission sppectroscoppy was carried out with Al K${\alpha}$ Line. The CdTe simiconductor was determined to be pp-typpe with low dopping concentration from Hall measurement. We found that there are two reacted pphases of Te with Eu (related to divalent Eu and trivalent Eu, resppectively) from least square fitting of Te 4d sppectra, but three is no indication of Cd reaction. Trivalent Eu exists after roughly one monolayer depposition (600 sec. depposition time is considered as one monolayer), which is also observed at Eu 3d core level sppectra. Overlayer Eu is metallized after roughly 2 monolayers depposition, as can be deduced from the fact that metallic edge near Fermi level begins to appear. The intensity of core-level of Te decreases expponentially at the initial stage (near one monolayer) and after one monolayer depposition it decreases more slowly due to Te out-diffusion. We categorized the growth mode of Eu on CdTe as S-K growth mode (cluster formation after one monolayer deppisition) from the relative intensity pplot of Te 4d normalized to the cleaved surface. At cleaved surface band bending is already established due to surface defects. At first 100 sec. depposition time the shift toward lower binding side by 0.6 eV is found at all core level sppectra of all elements in semiconductor. This shift is considered as the re-adjustment of surface Fermi level to the pposition induced by Eu metal (0.2 eV above the valence band maximum).