용액 결정성장하의 Nylon 4,6 의 결정구조 및 열적성질

Crystal structure and thermal properties of solution crystallized nylon 4,6

Calorimetric (D.S.C) studies were carried out on the nylon 4,6 single crystals grown from 1,4-butanediol solution at various crystallisation temperatures, based on the assessment of the lamellar thickness by small angle x-ray scattering. Samples were annealed mainly ot get rid of residual solvents inside the crystals. The effect of annealing on the crystal perfection is inferred from the measured thermal properties of the crystals. Accordig to the scanning rates less than 80 K/min., D. S C. melting peaks indicate that changes in the internal morphology of nylon 4,6 crystals preapred at different crystallisation temeratures yield a thermodynamic melting temperature. Tm, of 319 $^{\circ}C$, for the infinitely extended crystal thickness (1/ι). The obtained heat of fusion value for the inginite crystal thickness, Ho, was 270 J/g from the plot of measured feat of fusion ($\Delta$Hm) vs. reciprocal crystal thickness (1/ι). based on these values, the fold surface energy, $\delta$e. of 65.4 erg/$\textrm{cm}^2$ was obtained from Hoffman-Waeeks equation. The thermodynamic melting temperature and heat of fusion of the infinite crystal thickness for the solution grow nylon 4,6 single crystals are found to be higher than of the reported corresponding solution grown nylon 6,6 single crystals. pbtained crystallinity from D. S. C measurements ranges from 40 to 50 %, which is close to the reported yalue for the nylon 6,6 single ctystals but lower than we expected.