Abstract
$n^{+}$-p homojunction InP diodes were fabricated using thermal diffusion of Sulfur into p-type InP substrates(Zn doped, LEC grown, p=2.3${\times}$10$^{16}$c $m^{-3}$). The Sulfur diffusion was carried out at 550$^{\circ}C$, 600$^{\circ}C$, 700$^{\circ}C$ for 4 hours in a sealed quartz ampule(～2ml in volume) containing 5mg I $n_2$ $S_3$ and Img of red phosphorus. The formed junction depth was below 0.5$\mu\textrm{m}$. After the removal of diffused layer on the rear surface of the wafer, the beak ohmic contacts to the p-side were made with a vacuum evaporation of An-Zn(2%) followed by an annealing at 450$^{\circ}C$ for 5 minutes in flowing Ar gas. The front contacts were made with a vacuum evaporation of Au-Ge(12%) followed by an annealing at 500$^{\circ}C$ for 3 minutes in flowing Ar gas. The remarkable sprctral response of the cells obtained at the region of 6000-8000${\AA}$ region. The open circuit voltage $V_{oc}$ , short circuit current density $J_{sc}$ , fill factor and conversion efficiency η of the fabricated pattern solar cells(diffusion condition : at 700$^{\circ}C$ for 4 hours) were 0.660V, 14.04㎃/$\textrm{cm}^2$, 0.6536 and 10.09%, respectively.y.