Electrical Properties of PZT Thin Films Deposited on the Ru/$RuO_2$ Metal/Oxide Hybrid Electrodes (Ru/$RuO_2$ 금속/산화물 이중전극 위에 증착한 PZT 박막의 전기적 특성)

  • Jeong, Kyu-Won;Park, Young;Song, Joon-Tae
    • Journal of the Korean Institute of Electrical and Electronic Material Engineers
    • /
    • v.14 no.4
    • /
    • pp.281-288
    • /
    • 2001
  • PZT thin films (3500$\AA$) have been prepard on the Ru/Ru $O_2$ and Ru $O_2$ bottom electrodes with a RF magnetron sputtering system using P $b_{1.05}$(Z $r_{0.52}$, $Ti_{0.48}$) $O_3$ ceramic target. Ru/Ru $O_2$ bottom electrode was fabricated by in-situ processing controlled the $O_2$ partial pressure. The PZT thin films deposited on the Ru/Ru $O_2$ bottom electrode were preferred oriented (101) plane. The PZT thin films deposited on the Ru/Ru $O_2$ bottom electrodes showed better electrical properties than those with Ru $O_2$ bottom electrodes because Ru $O_2$ prevented oxygen vacancies and impurities from existing withing the interface and substrate.e.

  • PDF

Effect of Deposition Temperature and Oxygen on the Growth of $RuO_2$ Thin Films Deposited by Metalorganic Chemical Vapor Deposition (금속유기 화학증착법으로 증착시킨 $RuO_2$박막의 성장에 미치는 증착온도와 산소의 영향)

  • 신웅철;윤순길
    • Journal of the Korean Ceramic Society
    • /
    • v.34 no.3
    • /
    • pp.241-248
    • /
    • 1997
  • RuO2 thin films were deposited on SiO2(1000$\AA$)/Si and MgO(100) single crystal substrates at low tem-peratures by hot-wall metalorganic chemical vapor deposition(MOCVD), and effects of deposition paramet-ers on the properties of the thin films were investigated. RuO2 single phase was obtained at lower de-position temperature of 25$0^{\circ}C$. RuO2 thin films deposited onto SiO2(1000$\AA$)/Si substrates showed a random orientation, and RuO2 films onto MgO(100) single crystals showed the (hk0) orientation. The crystallinity and resistivity of RuO2 thin films increased and decreased with increasing deposition temperature, respec-tively. The resistivity of RuO2 thin films decreased with decreasing the flow rate. The resistivity of the 2600$\AA$-thick RuO2 thin films deposited with O2 flow rate of 50 sccm at 35$0^{\circ}C$ was 52.7$\mu$$\Omega$-cm, and they could be applicable to bottom electrodes of high dielectric materals.

  • PDF

Properties of sputtering PZT thin film on the Ru/$RuO_2$electrode (Ru/$RuO_2$전극에 성장한 PZT박막의 특성에 관한연구)

  • 강현일;최장현;이종덕;송준태
    • Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
    • /
    • /
    • pp.717-720
    • /
    • 2001
  • Ferroelectric lead ziroconate titanate (PZT) thin film were fabricated on the different bottom electrodes. Both Ru and Ru/RuO$_2$bottom electrodes were deposited by RF-magnetron sputteirng method. The structure phase and surface morphology of the PZT thin film were largely affected by the bottom electrode. It was observerd that used of Ru/RuO$_2$double electrode reduced leakage current and better ferroelectric properties compare with RuO$_2$bottom electrode. From these results, Ru/RuO$_2$hybride bottom electrode is thought to be the available structure for the bottom electrode.

  • PDF

A Study on the Plasma Etching of Ru Electrodes using $O_2/Cl_2$ Helicon Discharges

  • Kim, Hyoun-Woo;Hwang, Woon-Suk
    • Corrosion Science and Technology
    • /
    • v.2 no.4
    • /
    • pp.189-193
    • /
    • 2003
  • The Ru etching using $O_2/C_{12}$ plasmas has been studied by employing the helicon etcher. The changes of Ru etch rate, Ru to $SiO_2$ etch selectivity and Ru electrode etching slope with varied process variables were investigated. The Ru etching slope at the optimized etching condition was measured to be $84^{\circ}$. We reveal that the Ru etching using $O_2/C_{12}$ plasma generates the $RuO_2$ thin film. Possible mechanism of Ru etching is discussed.

Fabrication and Physical Properties of $RuO_2$ Thin Films ($RuO_2$ 박막의 제조와 물성)

  • 서동주;이재연;김건호
    • Journal of the Korean Vacuum Society
    • /
    • v.3 no.4
    • /
    • pp.442-448
    • /
    • 1994
  • 용액분무법으로 RuO2 박막을 석영 기판위에 성장시켰다. RuO2 박막의 결정구조는 정방 구조이 며 격자상수 a0=4.508 A, c0=3.092 A 이였다. RuO2 박막은 금속성 전도성을 나타냈다. RuO2박마의 광흡 수도는 후열처리함에 따라 증가하였고 박막의 광흡수도의 최소값은 후열처리 온도에 의존하지 않으며 에너지로 환산하면 ∼2.0eV로 거의 일정하였다. RuO2 박막의 후열처리의 온도와 후열처리 분위기가 기 판위에 성장된 RuO2 박막의 표면형태 grain 크기 grain 경계폭 전기적특성등에 영향을 미쳤다. RuO2 박 막이 실험실내의 공기중에 노출됨으로서 시료의 표면에 S와 C가 물리 흡착되었으며 sputtering 시간이 증가함에 따라 Ar+ 이온 빔의 충겨으로 RuO2가 부분적으로 환원되어 O원자의 피크 대 피크 높이가 감 소하여 O/Ru 의피크 높이의 비가 낮게 관측되었다.

  • PDF

Effect of RuO$_2$ Thin Film Microstructure on Characteristics of Thin Film Micro-supercapacitor ($RuO_2$박막의 미세 구조가 박막형 마이크로 슈퍼캐패시터의 특성에 미치는 영향)

  • Kim, Han-Ki;Yoon, Young-Soo;Lim, Jae-Hong;Cho, Won-Il;Seong, Tae-Yeon;Shin, Young-Hwa
    • Korean Journal of Materials Research
    • /
    • v.11 no.8
    • /
    • pp.671-678
    • /
    • 2001
  • All solid-state thin film micro supercapacitor, which consists of $RuO_2$/LiPON/$RuO_2$ multi layer structure, was fabricated on Pt/Ti/Si substrate using a $RuO_2$ electrode. Bottom $RuO_2$ electrode was grown by dc reactive sputtering system with increasing $O_2/[Ar+O_2]$ ratio at room temperature, and a LiPON electrolyte film was subsequently deposited on the bottom $RuO_2$ electrode at pure nitrogen ambient by rf reactive sputtering system. Room temperature charge-discharge measurements based on a symmetric $RuO_2$/LiPON/$RuO_2$ structure clearly demonstrates the cyclibility dependence on the microstructure of the $RuO_2$ electrode. Using both glancing angle x-ray diffraction (GXRD) and transmission electron microscopy (TEM) analysis, it was found that the microstructure of the $RuO_2$ electrode was dependent on the oxygen flow ratio. In addition, x- ray photoelectron spectroscopy(XPS) examination shows that the Ru-O binding energy is affected by increasing oxygen flow ratio. Furthermore, TEM and AES depth profile analysis after cycling demonstrates that the interface layer formed by interfacial reaction between LiPON and $RuO_2$ act as a main factor in the degradation of the cyclibility of the thin film micro-supercapacitor.

  • PDF

Thermal Stability of $\textrm{RuO}_2$ Thin Film Annealed at High Temperature in Oxygen Atmosphere ($\textrm{RuO}_2$ 박막의 산소 분위기 열처리시 열적 안정성에 관한 연구)

  • O, Sang-Ho;Park, Chan-Gyeong;Baek, Hong-Gu
    • Korean Journal of Materials Research
    • /
    • v.8 no.12
    • /
    • pp.1090-1098
    • /
    • 1998
  • $RuO_2$ thin films were deposited on Si and Ru/Si substrates by rf magnetron reactive sputtering and annealed in oxygen atmosphere(1atm) to investigate their thermal stability and diffusion barrier property. $RuO_2$ thin films were thermally stable up to 700\ulcorner for 10min. in oxygen atmosphere and showed excellent barrier property against the interdiffusion of silicon and oxygen. After annealing at $750^{\circ}C$ , however, volatilization to higher oxide occurred at the surface and inside of $RuO_2$ thin film and diffusion barrier property was also deteriorated. When annealed at $800^{\circ}C$, $RuO_2$thin film showed a different microstructure from that of $RuO_2$ thin film annealed at 75$0^{\circ}C$. It is likely that surface defect structure of $RuO_2$, $RuO_3$, and excess oxygen had an influence on the mode of volatilization with increasing annealing temperature.

  • PDF

Electrodic properties of PZT thin films growed on Ru/$RuO_2$ bottom eletrode (Ru/$RuO_2$ 하부전극에 성장한 PZT 박막의 전기적 특성 연구)

  • Choi, Jang-Hyun;Kang, Hyun-Il;Kim, Eung-Kwon;Park, Young;Song, Joon-Tae
    • Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
    • /
    • /
    • pp.58-62
    • /
    • 2002
  • Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ (PZT) thin films deposited on the Pt/Ti and Ru/$RuO_2$ bottom electrode by rf magnetron sputtering methode. Ru/$RuO_2$ bottom electrode deposited on the p-type wafer as Ru thickness by in-situ process. Our results show that all PZT films indicated perovskite polycrystalline structure with perferred orientation (110) and no pyrochlore phase is observed. A well-fabricated $RuO_2$/PZT/Ru(100nm)/$RUO_2$ capacitor showed a leakage current density in the order of $2.13{\times}10^{-7}A/cm^2$ as 100 kV/cm, a remanent polarization of 7.20 ${\mu}C/cm^2$, and a coercive field of 58.37 kV/cm. The results show that the new Ru/$RuO_2$ bottom electrodes are expected to reduce the degradation ferroelectric fatigue and excellent ferroelectric properties.

  • PDF

The study of the properties of PZT thin films deposited on $Ru/RuO_{2}$ electrode ($Ru/RuO_{2}$ 이중 전극위에 성장한 PZT 박막의 특성에 관한 연구)

  • Choi, Jang-Hyun;Kang, Hyun-Il;Park, Young;Somg, Joon-Tae
    • Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
    • /
    • /
    • pp.394-397
    • /
    • 2001
  • In this paper, in-situ deposited $Ru/RuO_2$ bottom electrodes have been investigated as new bottom electrodes for PZT thin film capacitor application. As a comparison, structural and electrical properties of PZT thin films on Pt/Ti and $RuO_2$ bottom electrodes are also investigated. The use of $Ru/RuO_2$ hybrid electrodes showed better electrical properties in compression with $RuO_2$ bottom electrode. With increasing Ru electrode thickness, the PZT thin films showed preferred orientation along the (110) direction and and leakage current of PZT thin films were improved. The PZT thin films on Ru (100nm)/$RuO_2$ electrodes exhibited excellent ferroelectric properties such as remant polarization and coercive field of $7.2C/cm^2$ and 46.35 kV/cm, respectively.

  • PDF

The study of the properties of PZT thin films deposited on Ru/RuO$_2$ electrode (Ru/RuO$_2$ 이중 전극위에 성장한 PZT 박막의 특성에 관한 연구)

  • Choi, Jang-Hyun;Kang, Hyun-Il;Park, Young;Song, Joon-Tae
    • Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
    • /
    • /
    • pp.394-397
    • /
    • 2001
  • In this paper, in-situ deposited Ru/RuO$_2$ bottom electrodes have been investigated as new bottom electrodes for PZT thin film capacitor application. As a comparison, structural and electrical properties of PZT thin films on Pt/Ti and RuO$_2$ bottom electrodes are also investigated. The use of Ru/RuO$_2$ hybrid electrodes showed better electrical properties in compression with RuO$_2$ bottom electrode. With increasing Ru electrode thickness, the PZT thin films showed preferred orientation along the (110) direction and leakage current of PZT thin films were improved. The PZT thin films on Ru (100nm)/RuO$_2$ electrodes exhibited excellent ferroelectric properties such as remant polarization and coercive field of 7.2 C/$\textrm{cm}^2$ and 46.35 kV/cm, respectively.

  • PDF