장기간 사용한 Cr-Mo강의 내식성 향상 방법에 관한 연구

A Study of Corrosion Resistance Improvement for Cr-Mo Steel in Long Term Service

  • 진영준 (충주대학교 항공.기계설계학과)
  • Jin, Yeung-Jun (Department of Aeronautical & Mechanical Design Engineering, Chungju National University)
  • 발행 : 2006.06.30

초록

It is no wonder that mechanical structures are accompanied by problems related to corrosion after being exposed to long hours of work. Corrosion of mechanical structures has been the most serious problem in the field of industry. The present study employed a laser beam irradiation test to improve the corrosion resistance of degraded Cr-Mo steel, which was used for more than 60,000 hours. To find the optimum irradiation test condition for the corrosion resistance of degraded Cr-Mo steel, hardness and residual stress measurements, micro-structural observation, and the electrochemical potentiokinetic reactivation (EPR) tests were performed with changes in laser beam test conditions including laser beam output, diameter, and velocity. Thus, the present study indicates that the optimum test condition and absorption energy for a laser beam test need to be determined to enhance corrosion resistance of degraded Cr-Mo steel.

참고문헌

  1. H. Kitagawa, J. D. Kwon, 'Degradation Problems in Life Prediction', Proceedings of the KSME/JSME Joint Conference, pp. 708-713, 1990
  2. H. Russell, 'Stress Corrosion Cracking/Materials Performance and Evaluation', Portland Or., pp. 363- 383, 1992
  3. H. Uhlig, 'Corrosion and Corrosion Control', John Wiley and Sons. Inc, pp. 178-186, 1984
  4. 오명, 강민호, '레이저 응용', 청문각, pp. 4-11, 1987
  5. R. Jimbou, M. Inagaki and T. Tamamua, 'Laser Heat Treatment' Japan Soc. Heat Treatment Vol. 21, No. 5, pp. 223-228, 1985
  6. Li Changchun, Zhou Yawen, Li Xiping and Li Guangxia, 'Fatigue Damage Evolution Law for Laser Beam Irradiated Cylindrical Specimens' Int. J. Fatigue 11 No. 3, pp. 183-186, 1989 https://doi.org/10.1016/0142-1123(89)90438-6
  7. 권재도, 진영준 등, '다단계 모의열화재의 재료강 도 평가와 수명예측', 대한기계학회 논문집, 제17 권, 제9호, pp. 2271-2279, 1993
  8. D. A. Jones, 'rinciples & Prevention of Corrosion' Macmillan Publishing Company, pp. 39-73, 1992
  9. ASTM G5-72, 'tandard Reference Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurement' pp. 1-11, 1972