The Fabrication and Properties of Lead-tree Transparent Dielectric Thick Films for PDP

PDP 무연 투명유전체 후막의 형성 및 특성

  • Published : 2004.10.01


Dry film method for large size of PDP(Plasma Display Panel) module has been actively investigated. This method for lead-free transparent dielectric formation depends on green sheet technology. By adjusting the composition of transparent dielectric powders and organics, uniformly dispersed slurry was fabricated, Viscosity of the slurry exhibited pseudoplastic behavior for tape casting, Cast green sheets were tested under tensile condition at room temperature. It was found that the increase in transparent dielectric powder and binder ratio leads to decrease in strain to failure of green sheets from 120 % to 34 % and from 255 % to 4 %, respectively. Tensile strength of green sheets decreased abruptly with increase of transparent dielectric powder ratio, with minimum at 0.13 MPa. On the other hand, tensile strength increased continuously from 0.1 MPa to 2.4 MPa with increase of binder ratio. The green sheets were attached on the glass substrate and heated by following firing schedule. As a result, the best result was obtained when fired at 580 $^{\circ}C$ for 15 min and had transmittance of 78 % in visible range 550 nm.


  1. 장명수, 류병길, 'PDP 재료 기술의 동향', 한국정보디스플레이학회지, 2권, 4호, p. 19, 2001
  2. H. S. Kim and B. H. Jung, 'Possible Glass Systems for Non-Pb Dielectric Layers, Barrier Rib and Sealant in PDP', The 3rd International Meeting on Information Display, p. 391, 2003
  3. 김형준, 김수길, 'AC-PDP 유전체 보호막의 연구 동향-', 전기전자재료학회지, 13권, 8호, p. 33, 2000
  4. A. Karas, T. Kumagai, and W. R. Cannon, 'Casting Behavior and Tensile Strength of Cast BaTiO3 Tape', Adv. Ceram. Mater., Vol. 3, No. 4, p. 374, 1998
  5. L. Braun, ]. R. Manis, and W. Tager Cannon, 'Viscosity of tape-casting slips', Am. Ceram. Soc. Bull., Vol. 64, No. 5, p. 727, 1995
  6. R. E. Milstler, D. J, Shanefield and R. B. Runk, 'Ceramic Processing before Firing', Wiley, p. 418, 1978
  7. R. E. Milster and E. R. Twiname, 'Tape Casting: theory and practice', Am. Ceram. Soc., p. 133, 2000