# 고온상태에서 Al 7075 합금의 크리이프 파단수명 예측에 대한 연구

• 강대민 (국립부산공업대학 산업안전과) ;
• 구양 (국립부산공업대학 기계과) ;
• 백남주 (부산대학교 생산기계과)
• Published : 1988.12.01

#### Abstract

Modern technological progress demands the use of materials at high temperature and high pressure. One of the most critical factors in considering such applications - perhaps the most critical one - is creep behavior. In this study the stress exponents n were determined during creep over the temperature range of $90^{\circ}C\;to\;500^{\circ}C$ (0.4 - 0.85 Tm) and stress range of 0.64 kgt/$mm^2$ in order to investigate the creep hehavior. The stress dependence of rapture time (n') were determined over the temperature range of $200^{\circ}C\;to\;240^{\circ}C$ and stress range of 8.13 kgt/$mm^2$ to 9.55 kgt/$mm^2$ in order to investigate to creep rupture property. And the stress transient dip tests were also carried out for the internal stress ${\sigma}i$ over the temperature range of $90^{\circ}C\;to\;500^{\circ}C$ and stress range of 0.64kgt/$mm^2$ to 17.2 kgt/$mm^2$. The creep tests for constant temperature and stress transient dip tests were conducted in air with Al 7075 alloy under constant tensile load. At around the temperature range $200^[\circ}C\;-\;230^{\circ}C$ and the stress level 8.13 - 9.55 (kgt/$mm^2$), the temperature range $280^{\circ}C\;-\;310^{\circ}C$ and the stress level 1.85 - 2.55 (kgt/$mm^2$), the temperature range $380^{\circ}C\;-\;410^{\circ}C$ and the stress 1.53 - 0.91 (kgt/$mm^2$), the stress exponent in had the value of 6.2 - 6.65 but at around the temperature range $90^{\circ}C\;-\;120^{\circ}C$ and the stress level 10 - 17.2(kgt/$mm^2$), the value of 1.3, and at around the temperature range $470^{\circ}C\;-\;500^{\circ}C$, the stress level 0.62 - 1.02 (kgt/$mm^2$) the value of 1-1. Besides these results, at around the temperature $200^{\circ}C\;-\;240^{\circ}C$ the stress dependence of rupture time (n') had the value of 6.3. Finally, it was found that the value n calculated by considering the applied stress dependence of the internal stress were in good agreement with those obtained for the creep test. Then, it was concluded that the change in n was mainly attributed to the difference of the applied stress dependence of the internal stress and the ratio of the internal stress to the applied stress, and the creep rupture life may be represented as.