# 연삭가공된 강재의 표면 Rolling시 가압력이 표면 조도에 미치는 영향

• Kim, Hee-Nam (Department of Mechanical Engineering, Myong-Ji University)
• 김희남 (명지대학교 기계공학과)
• Published : 1987.09.30
• 23 3

#### Abstract

The surface rolling method which is one of the plastic deformation processes increases the surface roughness with reduction of diameter and hardness. In this study, three NACHI 6000 ZZ bearing were used for surface rolling tool on a mild steel. The following results have been obtained with the mild steel. 1) The load is major factor in getting fine surface roughness of roller fininshing after grinding. The optimal surface roughness of SS40 steel can be obtained at the contact pressure of $210kgf/cm^2$. But, Better surface roughness can not be expected, Due to flaking phenomena at more than 300 kgf/cm of contact pressure. 2) At the contact pressure range of $200kgf/cm^2{\sim}210kgf/cm^2$ for optimal surface roughness, The surface hardness increased to Hv 200~Hv 240 from Hv 125 before surface rolling. 3) Within the diameter variation of $13{\mu}m$ the surface roughness and the surface hardness were increased, but out of variation of $14{\mu}m$. The surface roughness become worse and the surface hardness was increased.